2A14 Aluminum Bar
Product Name: 2A14 Aluminum Bar/2A14 Aluminum Rod
2A14 Aluminum Bar State: T4, T6, T351
Payment Terms: L/C, T/T, PayPal, Western Union
Product Name: 2A14 Aluminum Bar/Rod
State: T4, T6, T351
Payment Terms: L/C, T/T, PayPal, Western Union
Product Indroduction
The machinability is low after annealing: The corrosion resistance is not high, the anodic oxidation treatment and the coating method or the surface cladding aluminum layer are often used to improve the corrosion resistance.
Product Specifications
1. Diameter: Standard
2. Length: according to your requirements
3. CE & ISO
Product Data
Chemical Composition | ||||||||||
Alloy | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Al | Others |
Max | Max | Max | Max | Max | Max | Max | Max | Min | ||
2A14 | 0.6-1.2 | 0. 7 | 3.9-4.8 | 0.4-0.8 | 0.4-0.8 | 0.3 | 0.15 | The Remaining | 0.15 | |
Mechanical Properties | ||||
Aluminum Alloy & Temper | Tensile Strength Rm/Mpa | Proof Strength Rp0.2/Mpa | Percentage Elongation After Fracture A/% | Hardness HB |
2A14-T4 | ≥425 | ≥275 | 12 | 120 |
Product Application
2A14 is mainly used to produce various high load parts and components (but not including stamping parts forgings) such as aircraft skeleton parts, skin, bulkhead, wing ribs, wing beams, rivets and other 150 ℃ working parts.
Packaging&Delivery
1. Standard Exporting package.
2. Original package or neutral package.
3. According to clients ' needs.
4. Shipped in10-35 days after payment.
Our Shipping
Previous: 3A21 Aluminum Bar
Next: 2A50 Aluminum Bar